Pitting Resistance of Pure Fe-17%Cr Alloys : Consequences for Localized Corrosion Modeling (1995)
Boulleret, C., Pastol, J.-L., Bigot, J., Baroux, B., Gorse, D.
Pitting corrosion was observed on a high purity Fe-17Cr alloy in 0.02M NaCl solution of pH 6.6 at high anodic potential (+ 550 mV/SCE). Potentiostatic electrochemical noise measurements were...
Pitting Resistance of Pure Fe-17%Cr Alloys : Consequences for Localized Corrosion Modeling (1995)
Boulleret, C., Pastol, J.-L., Bigot, J., Baroux, B., Gorse, D.
Pitting corrosion was observed on a high purity Fe-17Cr alloy in 0.02M NaCl solution of pH 6.6 at high anodic potential (+ 550 mV/SCE). Potentiostatic electrochemical noise measurements were...
Pitting Resistance of Pure Fe-17%Cr Alloys : Consequences for Localized Corrosion Modeling (1995)
Boulleret, C., Pastol, J.-L., Bigot, J., Baroux, B., Gorse, D.
Pitting corrosion was observed on a high purity Fe-17Cr alloy in 0.02M NaCl solution of pH 6.6 at high anodic potential (+ 550 mV/SCE). Potentiostatic electrochemical noise measurements were...