NOVEL PERMANENT MAGNETIC MATERIALS MADE BY RAPID QUENCHING (1988)
Coehoorn, R., De Mooij, D., Duchateau, J., Buschow, K.
Two types of permanent magnetic materials were obtained by annealing melt spun flakes : (i) materials consisting mainly of Fe3B with Nd2Fe14B as a secondary phase, and (ii) materials based on...
NOVEL PERMANENT MAGNETIC MATERIALS MADE BY RAPID QUENCHING (1988)
Coehoorn, R., De Mooij, D., Duchateau, J., Buschow, K.
Two types of permanent magnetic materials were obtained by annealing melt spun flakes : (i) materials consisting mainly of Fe3B with Nd2Fe14B as a secondary phase, and (ii) materials based on...
NOVEL PERMANENT MAGNETIC MATERIALS MADE BY RAPID QUENCHING (1988)
Coehoorn, R., De Mooij, D., Duchateau, J., Buschow, K.
Two types of permanent magnetic materials were obtained by annealing melt spun flakes : (i) materials consisting mainly of Fe3B with Nd2Fe14B as a secondary phase, and (ii) materials based on...
MAGNETIC MEASUREMENTS ON R2Fe14B AND R2Co14B COMPOUNDS IN HIGH FIELDS (1985)
Sinnema, S., Franse, J., Radwanski, R., Buschow, K., De Mooij, D.
High field magnetisation measurements (up to 35 T) were performed on field-oriented samples of the tetragonal compounds R2Fe14B and R2Co14B at 4.2 K. Saturation magnetisation and anisotropy field...
MAGNETIC MEASUREMENTS ON R2Fe14B AND R2Co14B COMPOUNDS IN HIGH FIELDS (1985)
Sinnema, S., Franse, J., Radwanski, R., Buschow, K., De Mooij, D.
High field magnetisation measurements (up to 35 T) were performed on field-oriented samples of the tetragonal compounds R2Fe14B and R2Co14B at 4.2 K. Saturation magnetisation and anisotropy field...
MAGNETIC MEASUREMENTS ON R2Fe14B AND R2Co14B COMPOUNDS IN HIGH FIELDS (1985)
Sinnema, S., Franse, J., Radwanski, R., Buschow, K., De Mooij, D.
High field magnetisation measurements (up to 35 T) were performed on field-oriented samples of the tetragonal compounds R2Fe14B and R2Co14B at 4.2 K. Saturation magnetisation and anisotropy field...