Pore Structure Evolution of Lanthana–Alumina Systems Prepared through Coprecipitation (2000)
Nair, Jalajakumari, Nair, Dr. P., Mizukami, Fujio, Ommen Van, Dr. J.G., Doesburg, Giel B.M., Ross, Prof. J.R.H., ...
Pure Al2O3 and different compositions of La2O3–Al2O3 samples have been prepared through coprecipitation. Even after heating at 1300°C, the compositions La2O3·11Al2O3 and La2O3·13Al2O3 had higher...
Pore Structure Evolution of Lanthana–Alumina Systems Prepared through Coprecipitation (2000)
Nair, Jalajakumari, Nair, P., Mizukami, Fujio, Ommen Van, J.G., Doesburg, Giel B.M., Ross, J.R.H., ...
Pure Al2O3 and different compositions of La2O3–Al2O3 samples have been prepared through coprecipitation. Even after heating at 1300°C, the compositions La2O3·11Al2O3 and La2O3·13Al2O3 had higher...
Sintering of Lanthanum Zirconate (1999)
Nair, Jalajakumari, Nair, Dr. P., Doesburg, Giel B.M., Ommen Van, Dr. J.G., Ross, Prof. J.R.H., Burggraaf, Prof.dr.ir. A.J., ...
Lanthanum zirconate (La2Zr2O7) was prepared by coprecipitating lanthanum nitrate and zirconyl oxychloride at pH 10, followed by ethanol washing. The initial high surface area of 304 m2·g−1...
Sintering of Lanthanum Zirconate (1999)
Nair, Jalajakumari, Nair, P., Doesburg, Giel B.M., Ommen Van, J.G., Ross, J.R.H., Burggraaf, A.J., ...
Lanthanum zirconate (La2Zr2O7) was prepared by coprecipitating lanthanum nitrate and zirconyl oxychloride at pH 10, followed by ethanol washing. The initial high surface area of 304 m2·g−1...