Chen, Ir. C.S., Kruidhof, H., Bouwmeester, Dr. H.J.M., Verweij, Prof.dr.ir. H., Burggraaf, Prof.dr.ir. A.J.
Oxygen permeation measurements were performed on erbia-stabilized bismuth oxide-silver (40 v/o) composite membranes in the range of thickness of 1.60¿0.23 mm and temperature of 850¿650 °C. Air was...
Chen, Ir. C.S., Kruidhof, Ing. H., Bouwmeester, Dr. H.J.M., Verweij, Prof.dr.ir. H., Burggraaf, Prof.dr.ir. A.J.
Oxygen permeation measurements were performed on erbia-stabilized bismuth oxide-silver (40 v/o) composite membranes in the range of thickness of 1.60¿0.23 mm and temperature of 850¿650 °C. Air was...
Oxygen permeation through oxygen ion oxide-noble metal dual phase composites (1996)
Chen, Ir. C.S., Kruidhof, H., Bouwmeester, Dr. H.J.M., Verweij, Prof.dr.ir. H., Burggraaf, Prof.dr.ir. A.J.
Oxygen permeation behaviour of three composites, yttria-stabilized zirconia-palladium, erbia-stabilized bismuth oxidenoble metal (silver, gold) was studied. Oxygen permeation measurements were...
Oxygen permeation through oxygen ion oxide-noble metal dual phase composites (1996)
Chen, Ir. C.S., Kruidhof, Ing. H., Bouwmeester, Dr. H.J.M., Verweij, Prof.dr.ir. H., Burggraaf, Prof.dr.ir. A.J.
Oxygen permeation behaviour of three composites, yttria-stabilized zirconia-palladium, erbia-stabilized bismuth oxidenoble metal (silver, gold) was studied. Oxygen permeation measurements were...
Chen, Ir. C.S., Boukamp, Dr. B.A., Bouwmeester, Dr. H.J.M., Cao, Dr. G.Z., Kruidhof, H., Winnubst, Dr. A.J.A., ...
Yttria-stabilized cubic zirconia (YSZ)-palladium dual phase composites have been investigated. The percolative composite containing 40 vol% Pd (ZYPd40) showed a much larger oxygen permeability than...
Chen, Ir. C.S., Boukamp, Dr. B.A., Bouwmeester, Dr. H.J.M., Cao, Dr. G.Z., Kruidhof, H., Winnubst, Dr. A.J.A., ...
Yttria-stabilized cubic zirconia (YSZ)-palladium dual phase composites have been investigated. The percolative composite containing 40 vol% Pd (ZYPd40) showed a much larger oxygen permeability than...