Strain Rate Dependence on Mechanical Properties in Some Commercial Aluminum Alloys. (1998)
Higashi, K., Mukai, T., Kaizu, K., Tsuchida, S., Tanimura, S.
An investigation of flow stress and ductility as a function of stress rate at room temperature from 0.001 to 4000 1/s as conducted for some commercial aluminum alloys (1050, 3003, 3004, 5182 and...
Higashi, K., Mukai, T., Kaizu, K., Tsuchida, S., Tanimura, S.
The room temperature flow stress of aa 5182 was examined as a function of strain rates from 0.001/s to 4000/s at room temperature.
STRAIN RATE DEPENDENCE ON MECHANICAL PROPERTIES IN SOME COMMERCIAL ALUMINUM ALLOYS (1991)
Higashi, K., Mukai, T., Kaizu, K., Tsuchida, S., Tanimura, S.
The flow stress and ductility of some commercial aluminum alloys (1050, 3003, 3004, 5182 and 7N01) have been investigated as a function of strain rates over the range from 1x10-3 to 4x103s-1 at room...
Higashi, K., Mukai, T., Kaizu, K., Tsuchida, S., Tanimura, S.
The flow stress of a commercial 5182 aluminum alloy has been investigated as a function of strain rates in the range from 1x10-3 to 4x103s-1 at room temperature. The 5182 alloy exhibited the negative...
STRAIN RATE DEPENDENCE ON MECHANICAL PROPERTIES IN SOME COMMERCIAL ALUMINUM ALLOYS (1991)
Higashi, K., Mukai, T., Kaizu, K., Tsuchida, S., Tanimura, S.
The flow stress and ductility of some commercial aluminum alloys (1050, 3003, 3004, 5182 and 7N01) have been investigated as a function of strain rates over the range from 1x10-3 to 4x103s-1 at room...
Higashi, K., Mukai, T., Kaizu, K., Tsuchida, S., Tanimura, S.
The flow stress of a commercial 5182 aluminum alloy has been investigated as a function of strain rates in the range from 1x10-3 to 4x103s-1 at room temperature. The 5182 alloy exhibited the negative...
STRAIN RATE DEPENDENCE ON MECHANICAL PROPERTIES IN SOME COMMERCIAL ALUMINUM ALLOYS (1991)
Higashi, K., Mukai, T., Kaizu, K., Tsuchida, S., Tanimura, S.
The flow stress and ductility of some commercial aluminum alloys (1050, 3003, 3004, 5182 and 7N01) have been investigated as a function of strain rates over the range from 1x10-3 to 4x103s-1 at room...
Higashi, K., Mukai, T., Kaizu, K., Tsuchida, S., Tanimura, S.
The flow stress of a commercial 5182 aluminum alloy has been investigated as a function of strain rates in the range from 1x10-3 to 4x103s-1 at room temperature. The 5182 alloy exhibited the negative...