Catalytic Graphitization of Wood-Based Carbons with Alumina by Pulse Current Heating (2005)
Hata, T., Ishimaru, K., Fujisawa, M., Bronsveld, P., Vystavel, T., Hosson, J. De, ...
Japanese cedar was preheated at 500°C and subsequently mixed with 40 µm Al2O3 particles. A pulse current heating method was used for a 5-min carbonization step under a pressure of 50 MPa in order...
High resolution soft X-ray absorption spectroscopy for the chemical state analysis of Mn (2000)
Kawai, J, Mizutani, Y, Sugimura, T, Sai, M, Higuchi, T, Harada, Y, ...
OPTICAL REFLECTIVITY SPECTRA AND ELECTRONIC STRUCTURES IN Fe7Se8 AND Co7Se8 (1988)
Sato, K., Kida, H., Fujisawa, M., Kamimura, T.
Spectra of optical conductivity and UPS have been measured in single crystals of Fe7Se8 and Co7Se8. Experimental spectra in Fe7Se8 showed good correspondence with the DOS (density of state) spectrum...
OPTICAL REFLECTIVITY SPECTRA AND ELECTRONIC STRUCTURES IN Fe7Se8 AND Co7Se8 (1988)
Sato, K., Kida, H., Fujisawa, M., Kamimura, T.
Spectra of optical conductivity and UPS have been measured in single crystals of Fe7Se8 and Co7Se8. Experimental spectra in Fe7Se8 showed good correspondence with the DOS (density of state) spectrum...
OPTICAL REFLECTIVITY SPECTRA AND ELECTRONIC STRUCTURES IN Fe7Se8 AND Co7Se8 (1988)
Sato, K., Kida, H., Fujisawa, M., Kamimura, T.
Spectra of optical conductivity and UPS have been measured in single crystals of Fe7Se8 and Co7Se8. Experimental spectra in Fe7Se8 showed good correspondence with the DOS (density of state) spectrum...