Schmidt, A., Uytdenhouwen, Inge, Kuhnlein, W., Roedig, M., Linke, J., Hirai, T., ...
In the present study, the effect of disruptions on beryllium has been studied. Disruptions are simulated in the electron beam facility JUDITH by high energetic pulses of up to 250 MJ/m2. Under these...
Status of the EU R&D programme on the blanket-shield modules for ITER (2008)
Lorenzetto, P., Boireau, B., Boudot, C., Bucci, Ph., Frayssines, P. E., Furmanek, A., ...
Fusion Engineering and Design Vol.83 Nr.7 - 9, 1015 - 1019
Status of the EU R&D programme on the blanket-shield modules for ITER (2008)
Lorenzetto, P., Boireau, B., Boudot, C., Bucci, P., Frayssines, P. E., Furmanek, A., ...
Material erosion and redeposition during the JET MkIIGB-SRP divertor campaign (2006)
Kirschner, A., Philipps, V., Balden, M., Bonnin, X., Brezinsek, S., Coad, J.P., ...
Status of fabrication development for plasma facing components in the EU. (2003)
Daenner, W., Merola, M., Lorenzetto, P., Peacock, A., Bobin-Vastra, I., Briottet, L., ...
Proc.of the 6th Internat.Symp.on Fusion Nuclear Technology (ISFNT-6), San Diego, Calif., April 7-12, 2002
Examination of Creep-Fatigue Crack Growth in Alloy 800 at 700 Degrees C. (1998)
Pfaffelhuber, M., Roedig, M., Schubert, F., Nickel, H.
The damage accumulation rule was used to mathematically define the fatigue crack growth and creep crack growth interaction. The interaction is noted by the increase of the crack growth velocity over...
Fatigue and Creep Crack Growth of Alloy 800 and Alloy 617 at High Temperatures. (1998)
Roedig, M., Huthmann, H., Hartnagel, W.
This paper presents an evaluation of several experiments involving creep crack growth and fatigue crack growth in X10NiCrAl32 20 (Alloy 800) and NiCr23Co12Mo (Alloy 617). Specimens were tested at...