Temperature Effects on the Strength and Toughness of Be12Nb. (1998)
Bruemmer, Stephen M., Arey, Bruce W., Jacobson, Rodney E.
Strength and toughness of single-phase Be12Nb have been assessed at temperatures from ambient to 1200 C using four-point-bend and hardness tests; vacuum-hot-pressed beryllide exhibits low bend...
Elevated Temperature Mechanical Properties of Be12Nb. (1998)
Jacobson, Rodney E., Bruemmer, Stephen M.
Bend strength, compression strength, fracture toughness, hot hardness and indentation creep behavior of single-phase, vacuum hot pressed and hot isostatically pressed (HIP) Be12Nb have been assessed...
Strength and Toughness of Be12Nb, Be17Nb2 and Two-Phase Be12Nb-Be17Nb2. (1998)
Bruemmer, Stephen M., Arey, Bruce W.
Bend strength, compression strength, and fracture toughness of Be12Nb and Be17Nb2 compounds have been assessed from room temperature to 1200 C; HIPed Be12Nb showed significantly improved low- and...
Strength and Toughness of Be12Nb, Be17Nb2 and Two-Phase Be12Nb-Be17Nb2. (1998)
Bruemmer, Stephen M., Arey, Bruce W.
Bend strength, compression strength, and fracture toughness of niobium beryllide intermetallic compounds have been assessed at temperatures from ambient to 1200 c. hot-isostatically-pressed (hip)...
Strength and Toughness of Single-Phase and Dual-Phase High-Temperature Intermetallics. (1998)
Bruemmer, Stephen M., Brimhall, John L.
The strength and toughness of several high-temperature beryllium-niobium (be12nb and be17nb2) and iridium-niobium (ir3nb) intermetallic compounds have been evaluated. materials were prepared by...
Effects of irradiation on intergranular stress corrosion cracking (1994)
Was, Gary S., Bruemmer, Stephen M.
Intergranular stress corrosion cracking (IASCC) is a pervasive and generic problem in current light water reactor and advanced reactor designs that can lead to widespread component failure. IASCC is...
Bruemmer, Stephen M., Was, Gary S.
This review paper examines mechanisms controlling IGSCC in selected LWR components. Emphasis is placed on identifying material microstructures and microchemistries which promote susceptibility to...
Quantitative analysis of radiation-induced grain-boundary segregation measurements (1994)
Carter, R. D., Damcott, D. L., Atzmon, Michael, Was, G. S., Bruemmer, Stephen M., Kenik, E. A.
Radiation-induced and precipitation-induced grain-boundary segregation profiles are routinely measured by scanning-transmission electron microscopy using energy-dispersive X-ray spectroscopy...